SA645GrA SA645GrB SA-645/SA-645M Specification for Pressure Vessel Plates, 5% and 5.5% Nickel Alloy Steels, Specially Heat Treated for low or cryogenic temperature service.
(Identical with ASTM Specification A645/A645M-10(2016).)
1.1 This specification covers specially heat treated 5 % and 5½ % nickel alloy steel plates intended primarily for welded pressure vessels for service at low or cryogenic temperatures.
1.2 The maximum thickness of plates which can be supplied under this specification is limited only by the capacity of the material to meet the specified requirements.
1.3 This material is susceptible to magnetization. Use of magnets in handling after heat treatment should be avoided if residual magnetism would be detrimental to subsequent fabrication or service.
1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
3.1 Plates supplied to this material specification shall conform to Specification A20/A20M. These requirements outline the testing and retesting methods and procedures, permitted variations in dimensions and mass, quality and repair of defects, marking, loading, and ordering information.
3.2 In addition to the basic requirements of this specification, certain supplementary requirements are available when additional control, testing, or examination is required to meet end use requirements. The purchaser is referred to the listed supplementary requirements in this specification and to the detailed requirements in Specification A20/A20M.
3.3 If the requirements of this specification are in conflict with the requirements of Specification A20/A20M, the requirements of this specification shall prevail.
4.1 Steelmaking Practice — The steel shall be killed and shall conform to the fine austenitic grain size requirements of Specification A20/A20M.
5.1 Grade A plates shall be heat treated in accordance with 5.2. Grade B plates shall be heat treated in accordance with 5.3. Shell plates and other parts, including heads and reinforcing pads that are heated above 1125°F [605°C] for forming, shall be heat treated after forming.
The plates shall be heated to a temperature within the range from 1575 to 1675°F [855 to 915°C], held within that temperature range for a minimum of 1 h/in. [2.4 min/mm] of thickness, but in no case less than 15 min, and then water-quenched to below 300°F [150°C].
The plates shall be reheated to a temperature within the range from 1275 to 1400°F [690 to 760°C], held within that temperature range for a minimum of 1 h/in. [2.4 min/mm] of thickness, but in no case less than 15 min, and then water-quenched to below 300°F [150°C].
The plates shall be reheated to a temperature within the range from 1150 to 1225°F [620 to 665°C], held within that temperature range for a minimum of 1 h/in. [2.4 min/mm] of thickness, but in no case less than 15 min, and then water-quenched or air cooled to below 300°F [150°C].
The plates shall be heated to a temperature within the range from 1470 to 1600°F [800 to 870°C], held within that temperature range for a sufficient time to obtain uniform temperature throughout the plate thickness, and then quenched in a liquid medium.
The plates shall be reheated to a temperature within the range from 1200 to 1330°F [650 to 720°C], held within that temperature range for a minimum of 1 h/in. [2.4 min/mm] of thickness, but in no case less than 15 min, and then water-quenched to below 300°F [150°C] for nominal plate thicknesses over ⅝ in. [16 mm], or cooled in air or water-quenched to below 300°F [150°C] for nominal plate thicknesses of ⅝ in. [16 mm] and under.
The plates shall be reheated to a temperature within the range from 1020 to 1150°F [550 to 620°C], held within that temperature range for a minimum of 30 min/in. [1.2 min/mm] of thickness, but in no case less than 15 min, and then water-quenched to below 300°F [150°C].
6.1 The steel shall conform to the chemical requirements given in Table 1 unless otherwise modified in accordance with Supplementary Requirement S17, Vacuum Carbon-Deoxidized Steel, in Specification A20/A20M.
| Element | Composition, % Grade A |
Composition, % Grade B |
|---|---|---|
| Carbon, max | ||
| Heat Analysis Product Analysis |
0.13 0.15 |
0.13 0.15 |
| Manganese | ||
| Heat Analysis Product Analysis |
0.30-0.60 0.25-0.66 |
0.90-1.50 0.84-1.59 |
| Phosphorus, max | ||
| Heat Analysis Product Analysis |
0.025 0.025 |
0.020 0.025 |
| Sulfur, max | ||
| Heat Analysis Product Analysis |
0.025 0.025 |
0.010 0.015 |
| Silicon | ||
| Heat Analysis Product Analysis |
0.20-0.40 0.18-0.45 |
0.15-0.30A 0.13-0.33A |
| Nickel | ||
| Heat Analysis Product Analysis |
4.8-5.2 4.7-5.3 |
5.0-6.0 4.9-6.1 |
| Chromium | ||
| Heat Analysis Product Analysis |
... ... |
0.10-1.00 0.06-1.05 |
| Molybdenum | ||
| Heat Analysis Product Analysis |
0.20-0.35 0.17-0.38 |
0.10-0.30 0.09-0.33 |
| Aluminum, total | ||
| Heat Analysis Product Analysis |
0.02-0.12 0.01-0.16 |
0.02-0.05 0.015-0.06 |
| Nitrogen, max | ||
| Heat Analysis Product Analysis |
0.020 0.025 |
0.010 0.010 |
| A The specified minimum limit does not apply if the total aluminum is 0.030 % or more, or if the acid soluble aluminum content is 0.025 % or more. | ||
7.1.1 The plates as represented by the tension test specimens shall conform to the requirements given in Table 2.
7.1.2 For nominal plate thicknesses of ¾ in. [20 mm] and under, the 1½ in. [40 mm] wide rectangular specimen may be used for the tension test, and the elongation may be determined in a 2 in. [50 mm] gage length that includes the fracture and that shows the greatest elongation.
| Property | Grade A | Grade B |
|---|---|---|
| Yield strength, min, ksi [MPa]A | 65 [450] | 85 [590] |
| Tensile strength, ksi [MPa] | 95-115 [655-795] | 100-120 [690-830] |
| Elongation in 2 in. [50 mm], min, %B | 20.0 | 20.0 |
|
A At 0.2 % offset, or, if agreed between the purchaser and the manufacturer, at 0.5 % extension under load. B See Specification A20/A20M for elongation adjustment. |
||
7.2.1 Charpy V-notch tests shall be made in accordance with the general requirements of Specification A20/A20M.
7.2.2 The longitudinal axis of the test specimens shall be transverse to the final direction of rolling of the plate.
7.2.3 Unless otherwise agreed, the plates shall be impact tested at the following temperatures:
7.2.4 Each specimen shall have a lateral expansion opposite the notch of not less than 0.015 in. [0.38 mm].
7.2.5 The values of energy absorption in foot-pounds-force [joules] and the fracture appearance in percent shear shall be recorded and reported for information.
8.1 alloy steel; alloy steel plate; pressure containing parts; pressure vessel steels; steel plates; steel plates for pressure vessel applications
A list of standardized supplementary requirements for use at the option of the purchaser is included in Specification A20/A20M. Supplementary requirements shall not apply unless specified in the order. Those which are considered suitable for use with this specification are listed below by title. Others enumerated in Specification A20/A20M may be used with this specification subject to agreement by the supplier.
Also listed below are additional supplementary requirements which are considered suitable for use with this specification.
S64.1 When required, the purchaser may specify longitudinal Charpy V-notch impact testing to energy-absorption acceptance criteria.
S64.2 Tests shall be conducted in accordance with the general requirements of Specification A20/A20M.
S64.3 The longitudinal Charpy V-notch impact properties shall not be less than those shown in Table S1.1.
S64.4 The impact values obtained on subsize specimens shall not be less than the values listed in Table S1.1.
| Size of Specimen, mm | Charpy V-notch Impact Value Required for Acceptance (Average of Three Specimens), ft-lbf [J] | Minimum Charpy V-notch Impact Value Without Requiring Retest (One Specimen Only of a Set), ft-lbf [J] |
|---|---|---|
| 10 by 10 | 25 [34] | 20 [27] |
| 10 by 7.5 | 19 [26] | 16 [22] |
| 10 by 6.67 | 17 [23] | 13 [18] |
| 10 by 5.0 | 13 [18] | 10 [14] |
| 10 by 3.33 | 8 [11] | 7 [10] |
| 10 by 2.50 | 6 [8] | 5 [7] |
S65.1 When required, the purchaser may specify transverse Charpy V-notch impact testing to energy-absorption acceptance criteria.
S65.2 Tests shall be conducted in accordance with the general requirements of Specification A20/A20M.
S65.3 The transverse Charpy V-notch impact properties shall not be less than those shown in Table S2.1.
S65.4 The impact values obtained on subsize specimens shall not be less than the values listed in Table S2.1.
| Size of Specimen, mm | Charpy V-notch Impact Value Required for Acceptance (Average of Three Specimens), ft-lbf [J] | Minimum Charpy V-notch Impact Value Without Requiring Retest (One Specimen Only of a Set), ft-lbf [J] |
|---|---|---|
| 10 by 10 | 20 [27] | 16 [22] |
| 10 by 7.5 | 15 [20] | 12 [16] |
| 10 by 6.6 | 13 [18] | 10 [14] |
| 10 by 5.0 | 10 [14] | 8 [11] |
| 10 by 3.33 | 7 [10] | 5 [7] |
| 10 by 2.50 | 5 [7] | 4 [5] |
Source: This specification interpretation is compiled from the Wugang Steel Spot standards library (sister site, reposted with permission). Copyright of the original standards belongs to each standards organization. For official use please refer to the published standard text.
Hongye Steel keeps 5,000+ tons in stock — cutting-to-drawing and nationwide delivery.